Pengaruh Metode Sintesis Silika Mesopori SBA-15 terhadap Analisis Differential Scanning Calorimetry dan Pengukuran Low Angles X-Ray Diffraction
DOI:
https://doi.org/10.31963/intek.v5i1.198Abstract
Mesoporous silica SBA-15 is an interesting material having highly ordered nanopores and large surface area, which is synthesized by sol gel and hydrothermal methods. In this study, mesoporous silica SBA-15 was synthesised with two different methods and the characteris was using X-Ray Diffraction (XRD) and Differential Scanning Calorimetry (DSC). SBA-15 was prepared TEOS as precursor and Pluronic 123 as surfactant. Thermoporous mesoporous DSC thermogram results of the SBA-15A mesoporous silica is (Tg 79oC and Tc 158oC). This is relatively lower than SBA-15B (Tg 86oC and Tc 158oC). The measurement of low angle X-Ray Diffraction SBA-15A has a crystal size 9.46 nm and SBA-15B has a crystal size 9.96 nm. The synthesis of SBA-15 using the hydrothermal method needs to be studied further to obtain thermal characteristics and a more stable crystal structureReferences
J. Wang, H. Ge, and W. Bao, “Synthesis and characteristics of
SBA-15 with thick pore wall and high hydrothermal stability,â€
Mater. Lett., vol. 145, pp. 312–315, Apr. 2015.
B. Lei et al., “Luminescent carbon dots assembled SBA-15 and
its oxygen sensing properties,†Sens. Actuators B Chem., vol.
, pp. 101–108, Jul. 2016.
T. P. B. Nguyen, J.-W. Lee, W. G. Shim, and H. Moon, “Synthesis of functionalized SBA-15 with ordered large pore size and its adsorption properties of BSA,†Microporous Mesoporous Mater., vol. 110, no. 2–3, pp. 560–569, Apr. 2008.
A. Katiyar, L. Ji, P. Smirniotis, and N. G. Pinto, “Protein adsorption on the mesoporous molecular sieve silicate SBA-15: effects of pH and pore size,†J. Chromatogr. A, vol. 1069, no. 1, pp. 119–126, 2005.
N. Rahmat, A. Z. Abdullah, and A. R. Mohamed, “A Review: Mesoporous Santa Barbara Amorphous-15, Types, Synthesis and Its Applications towards Biorefinery Production,†Am. J. Appl. Sci., vol. 7, no. 12, pp. 1579–1586, Dec. 2010.
E. M. Johansson, J. M. Córdoba, and M. Odén, “Synthesis and characterization of large mesoporous silica SBA-15 sheets with ordered accessible 18 nm pores,†Mater. Lett., vol. 63, no. 24–25, pp. 2129–2131, 2009.
L. Cao and M. Kruk, “Synthesis of large-pore SBA-15 silica from tetramethyl orthosilicate using triisopropylbenzene as micelle expander,†Colloids Surf. Physicochem. Eng. Asp., vol. 357, no. 1–3, pp. 91–96, Mar. 2010.
M. Kruk, M. Jaroniec, C. H. Ko, and R. Ryoo, “Characterization of the Porous Structure of SBA-15,†Chem. Mater., vol. 12, no. 7, pp. 1961–1968, Jul. 2000.